나노버블 CO2 용해 기술을 활용한 레미콘 회수수 처리 및 재이용 (Processing and Reuse of Ready-Mixed Concrete Recovered Water using Nano Nubble CO2 Dissolution Technology)

서지정보

· 발행기관 : 한국재료학회
· 수록지 정보 : 한국재료학회지 / 35권 / 5호 / 191 ~ 196페이지
· 저자명 : 김종규

초록

This research aimed to find an eco-friendly way to neutralize water recovered from ready-mixed concrete by dissolving carbon dioxide in it, and to verify the potential use of such water for mixing concrete. Carbon dioxide was injected using nanobubble technology into recovered water, and the optimized conditions for dissolution were established by analyzing the carbon dioxide concentration in the water and measuring pH over time. Mortar was manufactured using this recovered water following carbon dioxide nanobubbles treatment, and measurements of compressive strength and thermogravimetric analysis (TGA) were conducted to verify the formation of calcium carbonate. 2,464 mg/L of carbon dioxide was dissolved in the recovered water, and the pH was measured to be 6.34. The compressive strength of the manufactured mortar was found to be 32.02 % stronger than mortar manufactured with normal tap water. According to the thermogravimetric analysis results, the amount of calcium hydroxide produced in the mortar manufactured with recovered water from ready-mixed concrete was 8.10 %, and the production amount of calcium carbonate was 6.49 %. This means that the amount of calcium carbonate produced was greater than that in mortar manufactured with normal tap water, as well as tap water containing nanobubble carbon dioxide.
The carbon dioxide was stably dissolved in water recovered from ready-mixed concrete using nanobubbles, enabling environmentally friendly neutralization without the use of chemicals. Also, when the recovered water from ready-mixed concrete containing dissolved carbon dioxide was used for mixing concrete, it was determined that the carbonation reaction influenced the formation of calcium carbonate, which contributed to the improvement in concrete strength.

영어초록

This research aimed to find an eco-friendly way to neutralize water recovered from ready-mixed concrete by dissolving carbon dioxide in it, and to verify the potential use of such water for mixing concrete. Carbon dioxide was injected using nanobubble technology into recovered water, and the optimized conditions for dissolution were established by analyzing the carbon dioxide concentration in the water and measuring pH over time. Mortar was manufactured using this recovered water following carbon dioxide nanobubbles treatment, and measurements of compressive strength and thermogravimetric analysis (TGA) were conducted to verify the formation of calcium carbonate. 2,464 mg/L of carbon dioxide was dissolved in the recovered water, and the pH was measured to be 6.34. The compressive strength of the manufactured mortar was found to be 32.02 % stronger than mortar manufactured with normal tap water. According to the thermogravimetric analysis results, the amount of calcium hydroxide produced in the mortar manufactured with recovered water from ready-mixed concrete was 8.10 %, and the production amount of calcium carbonate was 6.49 %. This means that the amount of calcium carbonate produced was greater than that in mortar manufactured with normal tap water, as well as tap water containing nanobubble carbon dioxide.
The carbon dioxide was stably dissolved in water recovered from ready-mixed concrete using nanobubbles, enabling environmentally friendly neutralization without the use of chemicals. Also, when the recovered water from ready-mixed concrete containing dissolved carbon dioxide was used for mixing concrete, it was determined that the carbonation reaction influenced the formation of calcium carbonate, which contributed to the improvement in concrete strength.