자외선 조사량에 따른 태양전지 모듈 봉지재의 특성 분석 (Characterization of Photovoltaic Module Encapsulant According to UV Irradiation Dose)

서지정보

· 발행기관 : 한국태양광발전학회
· 수록지 정보 : Current Photovoltaic Research / 6권 / 3호 / 81 ~ 85페이지
· 저자명 : 이송은, 배준학, 신재원, 전찬욱

초록

The photovoltaic modules installed in the actual field are affected by various external environments and the electrical performance output value is generally lowered compared to initial output value. The most of photovoltaic modules consists of low iron glass, encapsulant (EVA), back sheet, frame and junction box assembly based on the solar cells. In this paper, the characteristics of encapsulant which is an important constituent material of photovoltaic module were verified by maximum power determination, electro luminescence images, yellowness index measurement, and gel content measurement after ultraviolet (UV) irradiation exposure. The most commonly installed 72 cells crystalline photovoltaic modules were tested after various UV exposure of 0, 15, 30, and 60 kWh/m2 and compared with the reference module. After UV exposure of 15 kWh/m2, which is the current international test condition, a small amount of change was observed in yellowness index and electroluminescence, while a gell content rapidly increased. At a cumulative dose of 60 kWh/m2, which will be a new international test condition in the near future, however, the yellowness index increased sharply and showed the greatest output power drop.

영어초록

The photovoltaic modules installed in the actual field are affected by various external environments and the electrical performance output value is generally lowered compared to initial output value. The most of photovoltaic modules consists of low iron glass, encapsulant (EVA), back sheet, frame and junction box assembly based on the solar cells. In this paper, the characteristics of encapsulant which is an important constituent material of photovoltaic module were verified by maximum power determination, electro luminescence images, yellowness index measurement, and gel content measurement after ultraviolet (UV) irradiation exposure. The most commonly installed 72 cells crystalline photovoltaic modules were tested after various UV exposure of 0, 15, 30, and 60 kWh/m2 and compared with the reference module. After UV exposure of 15 kWh/m2, which is the current international test condition, a small amount of change was observed in yellowness index and electroluminescence, while a gell content rapidly increased. At a cumulative dose of 60 kWh/m2, which will be a new international test condition in the near future, however, the yellowness index increased sharply and showed the greatest output power drop.

참고자료

· 없음